A Self-Assembled 2D Thermofunctional Material for Radiative Cooling.

Small 2019 Dec 25;15(52):e1905290. Epub 2019 Oct 25.

Catalan Institute of Nanoscience and Nanotechnology (ICN2), CSIC and BIST, Campus UAB, Bellaterra, 08193, Barcelona, Spain.

The regulation of temperature is a major energy-consuming process of humankind. Today, around 15% of the global-energy consumption is dedicated to refrigeration and this figure is predicted to triple by 2050, thus linking global warming and cooling needs in a worrying negative feedback-loop. Here, an inexpensive solution is proposed to this challenge based on a single layer of silica microspheres self-assembled on a soda-lime glass. This 2D crystal acts as a visibly translucent thermal-blackbody for above-ambient radiative cooling and can be used to improve the thermal performance of devices that undergo critical heating during operation. The temperature of a silicon wafer is found to be 14 K lower during daytime when covered with the thermal emitter, reaching an average temperature difference of 19 K when the structure is backed with a silver layer. In comparison, the soda-lime glass reference used in the measurements lowers the temperature of the silicon by just 5 K. The cooling power of this simple radiative cooler under direct sunlight is found to be 350 W m when applied to hot surfaces with relative temperatures of 50 K above the ambient. This is crucial to radiatively cool down devices, i.e., solar cells, where an increase in temperature has drastic effects on performance.
View Article and Find Full Text PDF

Download full-text PDF

Source
http://dx.doi.org/10.1002/smll.201905290DOI Listing
December 2019

Nanowire forest of pnictogen-chalcogenide alloys for thermoelectricity.

Nanoscale 2019 Jul;11(28):13423-13430

Institut Néel, CNRS, 25 avenue des Martyrs, F-38042 Grenoble, France. and Univ. Grenoble Alpes, Grenoble, France.

Pnictogen and chalcogenide compounds have been seen as high-potential materials for efficient thermoelectric conversion over the past few decades. It is also known that with nanostructuration, the physical properties of these pnictogen-chalcogenide compounds can be further enhanced towards a more efficient heat conversion. Here, we report the reduced thermal conductivity of a large ensemble of Bi2Te3 alloy nanowires (70 nm in diameter) with selenium for n-type and antimony for p-type (Bi2Te3-ySey and Bi2-xSbxTe3 respectively). The nanowire growth was carried out through electrodeposition in nanoporous aluminium oxide templates with high aspect ratios leading to a forest (109 per centimetre square) of nearly identical nanowires. The temperature dependence of thermal conductivity for the nanowire ensembles was acquired through a highly sensitive 3ω measurement technique. The change in the thermal conductivity of nanowires is largely affected by the roughness in addition to the size effect due to enhanced boundary scattering. The major factor that influences the thermal conductivity was found to be the ratio of the rms roughness to the correlation length of the nanowire. With a high Seebeck coefficient and electrical conductivity at room temperature, the overall thermoelectric figure of merit ZT allows the consideration of such forests of nanowires as efficient potential building blocks of future TE devices.
View Article and Find Full Text PDF